| Name | Silicon Nitride Thickness (microns) | Wafer Status | Notes | ||
| B1 | 0.94 | processed | web release test | ||
| B2 | 0.945 | processed | ditto | ||
| B3 | 0.95 | broken | LAM3 the destroyer | ||
| B4 | 0.955 | processed | "isopropanol" bubbles on gold pads | ||
| B5 | 0.965 | Mike's nefarious purpose | Mike | ||
| B6 | 0.98 | Mike's nefarious purpose | Mike | ||
| B7 | 0.985 | used | |||
| B8 | 0.995 | used | |||
| B9 | 1 | used | |||
| B10 | 1.02 | used | |||
| B11 | 1.02 | used | |||
| B12 | 1.03 | Jared | 1600 ang Al | ||
| B13 | 1.04 | Jared | 1600 ang Al | ||
| B14 | 1.04 | Jared | 1600 ang Al | ||
| B15 | 1.05 | Jared | 1600 ang Al | ||
| B16 | 1.06 | Erik | nitride etch calibration | ||
| B17 | 1.07 | Erik | nitride etch calibration | ||
| B18 | 1.08 | Jared/APEX (9-30-04) | |||
| B19 | 1.1 | Jared/APEX (9-30-04) | |||
| B20 | 1.11 | Jared/APEX (9-30-04) | |||
| B21 | 1.11 | Erik | |||
| B22 | 1.12 | Erik | |||
| B23 | 1.14 | Jared/APEX (10-28-04) | |||
| B24 | 1.13 | Jared/APEX (10-28-04) | |||
| C1 | 0.821 | bad | scratched/water marks | ||
| C2 | 0.835 | limbo? | Al Lead Test, coated in PR | ||
| C3 | 0.851 | bad | scratched/ water marks | ||
| C4 | 0.863 | focus test wafer | Jared | ||
| C5 | 0.88 | broken | Eaten by GCAWS | ||
| C6 | 0.888 | broken | Eaten by GCAWS | ||
| C7 | 0.898 | bad | sccratched/water marks | ||
| C8 | 0.907 | done | G-Line test, G-line bad | ||
| C9 | 0.915 | focus test wafer | Jared | ||
| C10 | 0.921 | done/released | finished wedge with slight flaws, now broken | ||
| C11 | 0.931 | done/released | first successful wedge | ||
| C12 | 0.94 | done/released | Xetch characterization | ||
| C13 | 0.949 | done/released | Xetch characterization | ||
| C14 | 0.958 | ||||
| C15 | 0.966 | done | Mike | ||
| C16 | 0.976 | done/released | Xetch characterization | ||
| C17 | 0.984 | done | Mike | ||
| C18 | 0.993 | done | Mike | ||
| C19 | 1 | done | Mike | ||
| C20 | 1.01 | done | Mike | ||
| C21 | 1.02 | done | Mike | ||
| C22 | 1.03 | done | Mike | ||
| D1 | 1.197 | jared (10-5-04) | Al/Ti only | ||
| D2 | 1.179 | jared (10-5-04) | Al/Ti only | ||
| D3 | 1.17 | jared (10-5-04) | Al/Ti only | ||
| D4 | 1.167 | jared (10-5-04) | Al/Ti only | ||
| D5 | 1.156 | jared (10-5-04) | Al/Ti only | ||
| D6 | 1.149 | jared (10-5-04) | Al/Ti only | ||
| D7 | 1.137 | jared (10-5-04) | Al/Ti only | ||
| D8 | 1.133 | jared (10-5-04) | Al/Ti only | ||
| D9 | 1.126 | jared (10-5-04) | Al/Ti only | ||
| D10 | 1.117 | Erik | |||
| D11 | 1.11 | Erik | |||
| D12 | 1.1 | Erik | |||
| D13 | 1.093 | jared (11-12-04) | Al/TI (bad?) | ||
| D14 | 1.089 | jared (11-12-04) | Al/TI (bad?) | ||
| D15 | 1.086 | jared (11-12-04) | Al/TI (bad?) | ||
| D16 | 1.08 | jared (11-12-04) | Al/TI (bad?) | ||
| D17 | 1.078 | used | potential wedges | ||
| D18 | 1.072 | used | potential wedges | ||
| D19 | 1.072 | used | potential wedges | ||
| D20 | 1.07 | used | potential wedges | ||
| D21 | 1.071 | used | potential wedges | ||
| D22 | 1.064 | used | potential wedges | ||
| D23 | 1.065 | used | potential wedges | ||
| D24 | 1.06 | used | potential wedges | ||
| E1 | 0.934 | processing (Nb, 1000 SiO2) | 150 um | ||
| E2 | 0.966 | processing (Nb, 1000 SiO2) | 150 um | ||
| E3 | 0.964 | broken | 150 um | ||
| E4 | 0.958 | broken | 150 um | ||
| E5 | 0.947 | broken | 150 um | ||
| E6 | 0.945 | processing (Nb, 1000 SiO2) | 150 um | ||
| E13 | 1.056 | processing (Nb, 1500 SiO2) | 300 um | ||
| E14 | 1.06 | processing (Nb, 1500 SiO2) | 300 um | ||
| E15 | 1.067 | spacer wafer | 300 um | ||
| E16 | 1.076 | spacer wafer | 300 um | ||
| E17 | 1.081 | spacer wafer | 300 um | ||
| E18 | 1.091 | spacer wafer | 300 um | ||
| E19 | 1.099 | spacer wafer | 300 um | ||
| E20 | 1.109 | spacer wafer | 300 um | ||
| E21 | 1.115 | 300 um | |||
| E22 | 1.127 | 300 um | |||
| E23 | 1.134 | 300 um | |||
| E24 | 1.143 | 300 um | |||
| F1 | 1.115 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F2 | 1.124 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F3 | 1.134 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F4 | 1.146 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F5 | 1.151 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F6 | 1.163 | Jared/APEX (9-30-04) | double polished 150 um | ||
| F7 | 1.17 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F8 | 1.181 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F9 | 1.194 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F10 | 1.204 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F11 | 1.213 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F12 | 1.216 | Jared/APEX (10-28-04) | double polished 150 um | ||
| F13 | 1.236 | double polished 150 um | |||
| G1 | 1.1013 | nitride tests | 500 um | ||
| G2 | 1.109 | nitride tests | 500 um | ||
| G3 | 1.1044 | nitride tests | 500 um | ||
| G4 | 1.1011 | nitride tests | 500 um | ||
| G5 | 1.0871 | nitride tests | 500 um | ||
| G6 | 1.0771 | nitride tests | 500 um | ||
| G7 | 1.0698 | nitride tests | 500 um | ||
| G8 | 1.0614 | nitride tests | 500 um | ||
| G9 | 1.0557 | Jared/APEX (11-22-04) | 500 um | ||
| G10 | 1.0482 | Jared/APEX (11-22-04) | 500 um | ||
| G11 | 1.041 | double polished 150 um | |||
| G12 | 1.0311 | double polished 150 um | |||
| G13 | 1.0257 | double polished 150 um | |||
| G14 | 1.0212 | double polished 150 um | |||
| G15 | 1.0139 | double polished 150 um | |||
| G16 | 1.0104 | double polished 150 um | |||
| G17 | 1.0077 | double polished 150 um | |||
| G18 | 1.0021 | Jared/APEX (11-22-04) | double polished 150 um | ||
| G19 | 1.0011 | Jared/APEX (11-22-04) | double polished 150 um | ||
| G20 | 0.9977 | Jared/APEX (11-22-04) | double polished 150 um | ||
| G21 | 0.9944 | Jared/APEX (11-22-04) | double polished 150 um | ||
| G22 | 0.9925 | Jared/APEX (11-22-04) | double polished 150 um | ||
| G23 | 0.9845 | Jared/APEX (11-22-04) | double polished 150 um | ||
| H1 | 1.0716 | sherry? | 500 um | ||
| H2 | 1.0546 | sherry? | 500 um | ||
| H3 | 1.0579 | sherry? | 500 um | ||
| H4 | 1.0605 | sherry? | 500 um | ||
| H5 | 1.0635 | Jared nitride tests (2-10-05) | 500 um | ||
| H6 | 1.0696 | Jared nitride tests (2-10-05) | 500 um | ||
| H7 | 1.0709 | Jared nitride tests (2-10-05) | 500 um | ||
| H8 | 1.0713 | Jared nitride tests (2-10-05) | 500 um | ||
| H9 | 1.0772 | more nitride tests | 500 um | ||
| H10 | 1.0808 | more nitride tests | 500 um | ||
| H11 | 1.0832 | more nitride tests | 500 um | ||
| H12 | 1.0897 | more nitride tests | 500 um | ||
| H13 | 1.0968 | External gold vendor test | 500 um | ||
| H14 | 1.1109 | Jared/APEX(8-29-05) | 500 um | ||
| H15 | 1.1142 | Jared/APEX(8-29-05) | 500 um | ||
| H16 | 1.1214 | jared tests | 500 um | ||
| H17 | 1.1312 | jared tests | 500 um | ||
| H18 | 1.1372 | jared tests | 500 um | ||
| H19 | 1.1502 | jared tests | 500 um | ||
| H20 | 1.1582 | jared tests | 500 um | ||
| H21 | 1.695 | jared tests | 500 um | ||
| H22 | 1.1785 | jared tests | 500 um | ||
| H23 | 1.1904 | jared tests | 500 um | ||
| H24 | 1.1988 | jared tests | 500 um | ||
| H25 | 1.2156 | MIA | 500 um | ||
| I1 | 1.071 | Ptherm test wafer | |||
| I2 | 1.075 | Mike | |||
| I3 | 1.078 | Mike | |||
| I4 | 1.078 | Mike | |||
| I5 | 1.079 | Mike | |||
| I6 | 1.081 | Jared/APEX(8-29-05) | |||
| I7 | 1.086 | Jared/APEX(8-29-05) | |||
| I8 | 1.089 | Jared/APEX(8-29-05) | |||
| I9 | 1.093 | Jared/APEX(8-29-05) | |||
| I10 | 1.095 | Jared/APEX(8-29-05) | |||
| I11 | 1.099 | Jared/APEX(5-18-05) | |||
| I12 | 1.109 | Jared/APEX(5-18-05) | |||
| I13 | 1.115 | Jared/APEX(5-18-05) | |||
| I14 | 1.124 | Jared/APEX(5-18-05) | |||
| I15 | 1.134 | Jared/APEX(5-18-05) | |||
| I16 | 1.14 | Jared/APEX(5-18-05) | |||
| I17 | 1.151 | Jared/APEX(5-18-05) | |||
| I18 | 1.16 | Jared/APEX(5-18-05) | |||
| I19 | 1.168 | jared | xetch tests | ||
| I20 | 1.174 | jared | xetch tests | ||
| I21 | 1.185 | jared | xetch tests | ||
| I22 | 1.195 | Erik | Xetch characterization | ||
| I23 | 1.205 | erik | Xetch characterization | ||
| I24 | 1.214 | erik | Xetch characterization | ||
| I25 | 1.227 | Erik | Xetch characterization | ||
| J1 | 1.08 | APEX (6-20-05) | |||
| J2 | 1.08 | APEX (6-20-05) | |||
| J3 | 1.09 | APEX (6-20-05) | |||
| J4 | 1.09 | APEX (6-20-05) | |||
| J5 | 1.09 | APEX (6-20-05) | |||
| J6 | 1.09 | APEX (6-20-05) | |||
| J7 | 1.1 | APEX (6-20-05) | |||
| J8 | 1.1 | APEX (6-20-05) | |||
| J9 | 1.11 | APEX (6-20-05) | |||
| J10 | 1.11 | APEX (6-20-05) | |||
| J11 | 1.12 | APEX (6-20-05) | |||
| J12 | 1.13 | APEX (6-20-05) | |||
| J13 | 1.14 | APEX (6-20-05) | |||
| J14 | 1.14 | aborted reverse TES litho run | |||
| J15 | 1.15 | aborted reverse TES litho run | |||
| J16 | 1.16 | aborted reverse TES litho run | |||
| J17 | 1.17 | aborted reverse TES litho run | |||
| J18 | 1.18 | aborted reverse TES litho run | |||
| J19 | 1.19 | aborted reverse TES litho run | |||
| J20 | 1.2 | aborted reverse TES litho run | |||
| J21 | 1.21 | aborted reverse TES litho run | |||
| J22 | 1.22 | aborted reverse TES litho run | |||
| J23 | 1.23 | aborted reverse TES litho run | |||
| J24 | 1.25 | aborted reverse TES litho run | |||
| J25 | 1.26 | aborted reverse TES litho run | |||
| K1 | 1.25 | 150 um | |||
| K2 | 1.24 | 150 um | |||
| K3 | 1.23 | 150 um | |||
| K4 | 1.23 | 150 um | |||
| K5 | 1.22 | 150 um | |||
| K6 | 1.22 | 150 um | |||
| K7 | 1.21 | 150 um | |||
| K8 | 1.21 | 150 um | |||
| K9 | 1.2 | 150 um | |||
| K10 | 1.2 | 150 um | |||
| K11 | 1.19 | 150 um | |||
| K12 | 1.18 | 150 um | |||
| L1 | 1.2685 | Kam (8-8-05) | |||
| L2 | 1.2509 | Kam (8-8-05) | |||
| L3 | 1.2293 | Kam (8-8-05) | |||
| L4 | 1.2171 | Kam (8-8-05) | |||
| L5 | 1.2055 | Kam (8-8-05) | |||
| L6 | 1.1964 | Kam (8-8-05) | |||
| L7 | 1.1836 | Kam (8-8-05) | |||
| L8 | 1.1756 | Kam (8-8-05) | |||
| L9 | 1.1627 | Kam (9-7-05) | |||
| L10 | 1.1555 | Kam (9-7-05) | |||
| L11 | 1.1442 | Kam (9-7-05) | |||
| L12 | 1.1342 | Kam (9-7-05) | |||
| L13 | 1.1245 | Kam (9-7-05) | |||
| L14 | 1.1142 | Kam (9-7-05) | |||
| L15 | 1.1055 | Jared | Edge TES run | ||
| L16 | 1.1021 | Jared | Edge TES run | ||
| L17 | 1.0947 | Jared | Edge TES run | ||
| L18 | 1.0913 | Jared | Edge TES run | ||
| L19 | 1.088 | Jared | Edge TES run | ||
| L20 | 1.0794 | Jared | Edge TES run | ||
| L21 | 1.0777 | Kam (9-28-05) | |||
| L22 | 1.0753 | Kam (9-28-05) | |||
| L23 | 1.0712 | Gave to Miguel | |||
| L24 | 1.0706 | Kam (10-24-05) | |||
| L25 | 1.0668 | ||||